JIANG Xin-hong1,DUAN Long-chen1,LIU Zhi-yi1

• 1:中国地质大学工程学院
• 2:中国地质大学工程学院
• 3:中国地质大学工程学院 湖北武汉430074
• 4:湖北武汉430074

摘要(Abstract)：

采用双喷嘴闭路循环试验装置,测试了钻头胎体材料在泥浆冲蚀作用下所产生的总质量损失TML和由纯机械冲刷作用所产生的质量损失E。通过计算得到了由腐蚀及机械冲刷与腐蚀相互作用所产生的质量损失C+S。结果表明,钻头胎体材料的冲蚀磨损不是纯由机械冲刷作用引起,而是由机械冲刷、腐蚀及他们的相互作用共同引起。因此,在有腐蚀性的泥浆中设计和选用PDC(金刚石复合片)钻头时,除了考虑胎体材料的抗冲刷磨损性能外,还应考虑钻头胎体材料的抗腐蚀性。
In oil drilling the erosion and corrosion resistance of the matrix is one of the key factors affecting the quality of PDC bits.In order to understand the degradation mechanism of matrix materials for drill bits,a kind of loop recirculation rig is adopted to measure total mass loss TML,mass loss E by pure mechanical erosion,and then through calculation the mass loss C+S by corrosion and their synergy is obtained.The tested and calculated results show that TML of matrix materials is not only caused by pure mechanical erosion,but also by corrosion and their synergy of mechanical erosion and corrosion,which tells us that the corrosion resistance of matrix materials should be considered carefully besides their erosive resistance in the design and selection of PDC drill bits used in the corrosive drilling mud.

关键词(KeyWords)： 钻井泥浆;PDC钻头;胎体材料;冲蚀磨损
drilling mud;PDC drill bit;matrix materials;erosion and corrosion

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 江新洪,段隆臣,刘志义
JIANG Xin-hong1,DUAN Long-chen1,LIU Zhi-yi1

参考文献(References)：

• [1]陶长有,赵金英.PDC钻头失效的技术经济分析[J].大庆石油学院学报,1996,20(4):82-85.
• [2]王瑞和,沈忠厚.PDC钻头冲蚀机理分析与研究[J].石油钻采工艺,1992(3):25-28.
• [3]TOMA D,BRANDL W,MARGINEAN G.Wear and corrosion behav-iour of thermally sprayed cermet coatings;surface and coating technolo-gy[J].wear,2001(138):149-158.
• [4]BJORDAL M,BARDAL E,ROGNE T,et al.Erosion and corrosionproperties of WC coatings and duplex stainless steel in sand-contain-ing synthetic sea water[J].wear,1995(186-187):508-514.
• [5]NEVILLE A,REYES M,HODGKIESS T,et al.Mechanisms of wearon a Cobalt-base alloy in liquid-solid slurries[J].wear,2000(238):138-150.
• [6]REYES M,NEVILLE A.Degradation mechanisms of Co-based alloyand WC metal-matrix composites for drilling tools offshore[J]wear,2003(255):1143-1156.
• [7]KEMBAIYAN K T,KESH KESHAVEN.Combating severe fluid ero-sion and corrosion of drilling bits using thermal spray coatings[J].wear,1995(186-187):487-492.

文章评论(Comment)：